Corrosion resistant TiO2 film formed on magnesium by liquid phase deposition treatment

Files in This Item:
EA56-20_7180-7188.pdf2.35 MBPDFView/Open
Please use this identifier to cite or link to this item:

Title: Corrosion resistant TiO2 film formed on magnesium by liquid phase deposition treatment
Authors: Fujita, R. Browse this author
Sakairi, M. Browse this author →KAKEN DB
Kikuchi, T. Browse this author
Nagata, S. Browse this author
Keywords: Magnesium
Corrosion behavior
Liquid phase deposition
Issue Date: 1-Aug-2011
Publisher: Elsevier
Journal Title: Electrochimica Acta
Volume: 56
Issue: 20
Start Page: 7180
End Page: 7188
Publisher DOI: 10.1016/j.electacta.2011.03.146
Abstract: Liquid phase deposition treatment (LPD) was applied to form a corrosion protective titanium dioxide (TiO2) film on commercially available pure magnesium. Changing the solution pH, from acidic to highly alkaline, and with the addition of sucrose, it becomes possible to form a highly adhesive and thin TiO2 film on commercially available pure magnesium without any heat treatment. The role of the sucrose may be attributed to the formation of tetrafluoroboric acid (BF4)- in the solution reducing the homogeneous nucleation of TiO2 in the LPD solution. The film formed in the weak alkaline environment shows better corrosion resistance than at other LPD conditions, while the average rest potential is the same as that of as-polished specimens. This low rest potential may be due to micro-cracks in the formed film and high activity of the magnesium substrate.
Type: article (author version)
Appears in Collections:工学院・工学研究院 (Graduate School of Engineering / Faculty of Engineering) > 雑誌発表論文等 (Peer-reviewed Journal Articles, etc)

Submitter: 坂入 正敏

Export metadata:

OAI-PMH ( junii2 , jpcoar )

MathJax is now OFF:


 - Hokkaido University