CVD法によりTiB2/TiN二層被覆したSKD61鋼の溶融Alにおける耐浸食性

Files in This Item:
51(6) 640.pdf1.72 MBPDFView/Open
Please use this identifier to cite or link to this item:http://hdl.handle.net/2115/74942

Title: CVD法によりTiB2/TiN二層被覆したSKD61鋼の溶融Alにおける耐浸食性
Other Titles: Improvement of Corrosion Resistivity for a Melted Aluminum Alloy of SKD 61 Steel by a TiB2/TiN Bilayered Coating Formed by Chemical Vapor Deposition
Authors: 佐藤, 忠夫1 Browse this author
堀米, 毅2 Browse this author
上田, 幹人3 Browse this author →KAKEN DB
Authors(alt): Sato, Tadao1
Horigome, Takeshi2
Ueda, Mikito3
Keywords: TiB2/TiN
CVD Coating
Corrosion
Resistivity
in Melted Aluminum
Issue Date: 1-Jun-2000
Publisher: 表面技術協会
Journal Title: 表面技術
Journal Title(alt): Journal of the Surface Finishing Society of Japan
Volume: 51
Issue: 6
Start Page: 640
End Page: 645
Publisher DOI: 10.4139/sfj.51.640
Abstract: TiB2 and TiN films were coated by chemical vapor deposition on SKD 61 steel to improve the corrosion resistivity of a diecasting machine in a melted aluminum alloy. The protectivity of the film in the melted aluminum alloy was examined by an immersion test at 900°C and a thermal cycle test between room temperature and 900°C. TiN film, which serves as a binder, greatly improves the adhesion of TiB2 film on the steel substrate. The thermal cycle test indicated that the optimum thickness of TiB2 and TiN layers is at 4 and 6μm, respectively. Compared to ion-nitrized steel, steel coated by TiB2/TiN exhibits significantly higher degree of corrosion resistivity.
Type: article
URI: http://hdl.handle.net/2115/74942
Appears in Collections:工学院・工学研究院 (Graduate School of Engineering / Faculty of Engineering) > 雑誌発表論文等 (Peer-reviewed Journal Articles, etc)

Submitter: 上田 幹人

Export metadata:

OAI-PMH ( junii2 , jpcoar_1.0 )

MathJax is now OFF:


 

 - Hokkaido University