Nano-scratching in solution to the single-crystal Ta (100) subjected to anodic oxidation

英語

2006-08-07

IOP Publishing Ltd.

Journal of Physics D Applied Physics

39(15)

3150-3156

A single crystal-tantalum (100) surface was anodically oxidized at 5.0 V (SHE) for 1 h in pH 8.4 borate buffer solution. Nano-scratching in solution at a constant normal force of 300 µN was performed on the tantalum (100) surface kept at 5.0 V (SHE) after anodic oxidation. Nano-scratching in air was also performed on the tantalum (100) surface after anodic oxidation. A stick–slip was always observed in lateral force versus lateral displacement curves during nano-scratching in solution. The degree of stick–slip, however, decreased with increasing scratching rate. The average friction coefficient obtained with nano-scratching in solution was significantly larger than that obtained with nano-scratching in air and increased linearly with the logarithm of time required for scratching. In contrast, the friction coefficient obtained with nano-scratching in air was independent of the time required for scratching. The protrusion at the scratching end of the groove produced by nano-scratching in solution was observed from the AFM image, while no protrusion was observed for nano-scratching in air. It has been proposed that the protrusion consists of anodic oxide accumulated on the moving front of the indenter tip during nano-scratching in solution and contributes to the increase in lateral force, i.e. friction coefficient.

学術雑誌論文

Accepted Manuscript

Copyright © 2006 IOP Publishing Ltd.

0022-3727

1361-6463