Preparation of hydrophilic silicalite-1 nanocrystal-layered membranes and their application to separating water from water–acetone solution

英語

water-acetone solution

2008-10-01

Elsevier Science BV

Microporous and Mesoporous Materials

115(1-2)

176-183

Separation of water from a water-acetone solution was carried out by a pervaporation method using a hydrophilic silicalite-1 membrane. Silicalite-1 nanocrystals were piled up on the outer surface of cylindrical alumina ceramic filters, followed by a hydrothermal synthesis to form a silicalite-1 protection layer oil the nanocrystal layer. In other words, the membrane consisted of a silicalite-1 nanocrystal layer and a silicalite-1 protection layer (the nanocrystal-layered membrane). In order to achieve high hydrophilic properties of the membrane with the remaining silanol group, the liquid-phase oxidation technique was applied to remove the template. From the SEM observation, the nanocrystal layer and the protection layer were clearly observed, and the silicalitc-1 protection layer was uniformly formed on the nanocrystal layer. Pervaporation experiments to separate water from the water-acetone solution were conducted using the nanocrystal-layered membrane. It was considered that the secondary growth of the nanocrystals around the interface between the nanocrystal and protection layers affected the separation properties. The effects of the nanocrystal size oil the separation properties were examined. The membrane exhibited selective permeation as well as a high flux of water, and these properties were improved with a decrease in the size of the nanocrystals. Moreover, the layered membrane exhibited high hydrophilic properties regardless of the acetone concentrations. (C) 2008 Elsevier Inc. All rights reserved.

学術雑誌論文

Accepted Manuscript

1387-1811