Prediction of the diffusivity of cement-based materials using a three-dimensional spatial distribution model

英語

Micro-indentation

2012-03

Elsevier

Cement and Concrete Composites

34(3)

408-418

A three-dimensional image of hardened cement paste was reconstructed using a backscattered electron image (BEI) and used to predict the diffusion properties of hardened cement paste. After the BEI observations, an autocorrelation function (ACF) was calculated for each phase of the hardened cement paste, including the unhydrated cement, portlandite, and large pores. A three-dimensional image was reconstructed on the basis of the ACF based on random distributions. The dynamic elastic modulus and diffusion coefficient were calculated using a finite-element or finite difference method with the reconstructed three-dimensional images. The elastic modulus of the C-S-H phase was determined by micro-indentation, and the diffusivity of C-S-H was calculated using this elastic modulus based on previous reports. The resulting predicted dynamic elastic moduli and diffusion coefficients were in good agreement with the experimental results. Although, it was observed that the predicted values of the diffusivity of the blended cement pastes is different from the measured values, a new relationship between diffusivity and porosity of C-S-H in blended cement pastes was developed in this study.

学術雑誌論文

Accepted Manuscript

0958-9465

AA10770407