In Situ Electrochemical, Electrochemical Quartz Crystal Microbalance, Scanning Tunneling Microscopy, and Surface X-ray Scattering Studies on Ag/AgCl Reaction at the Underpotentially Deposited Ag Bilayer on the Au(111) Electrode Surface

英語

2011-06-30

American Chemical Society

Journal of Physical Chemistry C

115(25)

12471-12482

Ag/AgCl reaction at the Ag bilayer, which was underpotentially prepared on a Au(111) surface, was investigated using electrochemical quartz crystal microbalance (EQCM), scanning tunneling microscopy (STM), surface X-ray scattering (SXS), and electrochemical techniques. When the potential was scanned positively from -200 mV, the Cl^[-] ion was adsorbed on the Au(111) electrode surface around 0 mV, and then the phase transition of the adsorbed Cl^[-] ion layer from random orientation to (√3 x √3) structure took place at around +130 mV. The Ag bilayer and Cl^[-] ions were oxidatively reacted to form the AgCl monolayer with (√13 x √13)R13.9° structure around +200 mV, accompanied with the formation of AgCl monocrystalline clusters on the AgCl monolayer surface. The structure of the AgCl monolayer on the Au(111) surface was changed from (√13 x √13)R13.9° structure to (4 x 4) structure around +500 mV. When the potential was scanned back negatively, the AgCl monolayer was electrochemically reduced, and a Ag monolayer, not a bilayer, was formed on the Au(111) surface. In the subsequent potential cycles, the structural change between the Ag monolayer and the AgCl monolayer was reversibly observed. All oxidative structural changes were much slower than the reductive ones.

学術雑誌論文

Version of Record

1932-7447

1932-7455