Correlation between some physical properties of titanium dioxide particles and their photocatalytic activity for some probe reactions in aqueous systems

英語

2002-10-10

American Chemical Society

Journal of physical chemistry. B

106(40)

10501-10507

Nanocrystalline anatase titanium(IV) oxide (TiO2) particles were synthesized by hydrothermal crystallization in organic media (HyCOM) followed by calcination at various temperatures up to 1273 K, and they were characterized by analysis of surface adsorption of the substrates, as well as by X-ray diffraction (XRD) and Brunauer−Emmet−Teller (BET) surface area measurements. These HyCOM TiO2 samples were used for three kinds of photocatalytic reactions:  mineralization of acetic acid (AcOH) in aerated aqueous suspensions, dehydrogenation of 2-propanol (2-PrOH) by in situ platinized powders, and silver-metal deposition from silver ions (Ag+) in deaerated aqueous suspensions of bare TiO2 samples. Dependence of the photocatalytic activities on calcination temperature (Tc) and on the amount of adsorbed substrates in each reaction and correlations with the physical properties of HyCOM TiO2 were examined. In the case of mineralization of AcOH, the activitiy of each sample was almost proportional to the amount of surface-adsorbed AcOH in the dark, and the uncalcined (as-prepared) HyCOM TiO2 showed the highest activity, which was monotonically reduced with Tc, that is, with decrease in the amount of surface-adsorbed AcOH. On the other hand, in the case of silver-metal deposition, the photocatalytic activity was enhanced by calcination at higher temperature, despite the simultaneous decrease in the amount of surface-adsorbed Ag+ in the dark. Overall, the effects of calcination on the photocatalytic activities for several reaction systems strongly suggested that photocatalytic activity depends on two significant factors, adsorbability and recombination probability, corresponding to the specific surface area and crystallinity, respectively, and that the balance of these two factors determines the Tc dependence.

学術雑誌論文

Version of Record

1520-6106

AA11114073