MnO nanocrystals incorporated in a N-containing carbon matrix for Li ion battery anodes

英語

carbon

2016-03-16

Royal Society of Chemistry

RSC advances

6(36)

30445-30453

In this study, MnO nanocrystals incorporated in a N-containing carbon matrix were fabricated by the facile thermal decomposition of manganese nitrate-glycine gels. MnO/C composites with different carbon contents were prepared by controlling the initial ratio of manganese to glycine. The composition, phase structure and morphology of the composites were characterized by X-ray diffraction, X-ray photoelectron spectroscopy, Raman spectroscopy, scanning and transmission electron microscopy, and thermogravimetric analysis. The results indicated that MnO nanocrystals were uniformly embedded in the N-doped carbon matrix. The carbon matrix could effectively enhance the electrical conductivity of MnO and alleviate the strain arising from the discharge/charge cycling. The composite materials exhibited high discharge/charge capacities, superior cycling performance, and excellent rate capability. A high reversible capacity of 556 mA h g(-1) was obtained after 110 cycles of discharging and charging at a current rate of 0.5 A g(-1). Even at a high current rate of 3 A g(-1), the sample still delivered a capacity of around 286 mA h g(-1). The easy production and superior electrochemical properties enables the composites to be a promising candidate as an anode alternative for high-performance lithium-ion batteries.

学術雑誌論文

Accepted Manuscript

2046-2069