Reaction Mechanism of FePS3 Electrodes in All-Solid-State Lithium Secondary Batteries Using Sulfide-Based Solid Electrolytes

英語

sulfide

2018-09-15

The Electrochemical Society (ECS)

Journal of The Electrochemical Society

165(13)

A2948-A2954

In this study, we investigated the reaction mechanism of the FePS3 electrode in all-solid-state lithium secondary batteries that utilized sulfide-based solid electrolytes by X-ray diffraction patterns, X-ray absorption spectra, Raman spectra, and density-functional theory (DFT) calculations. In discharge-charge measurements, the reversible discharge-charge reaction (FePS3 + xLi+ + xe− ⇄ LixFePS3, 0 ⩽ x ⩽ 1.5) was confirmed. With this reaction, Li+-inserted FePS3 with low crystallinity was formed with the reduction of iron during the discharge cycle, and crystalline FePS3 appeared along with the oxidation of iron during the charge cycle. Raman spectra showed that P2S64− units were not destroyed during this discharge-charge cycle. In the second cycle, the discharge voltage of the batteries that used FePS3 increased relative to that at the first cycle. The reversible change in chemical states of iron and sulfur was confirmed by X-ray absorption. The first-principle calculation explained the experimental results of the change of crystalline phase and the increase in the discharge voltage. Further, the calculation results indicated that not only iron but also sulfur was oxidized and reduced from the first charge cycle onwards.

学術雑誌論文

Accepted Manuscript

© The Electrochemical Society, Inc. 2018. All rights reserved. Except as provided under U.S. copyright law, this work may not be reproduced, resold, distributed, or modified without the express permission of The Electrochemical Society (ECS). The archival version of this work was published in J. Electrochem. Soc. 2018 volume 165, issue 13, A2948-A2954.

0013-4651

1945-7111