Vis-Responsive Copper-Modified Titania for Decomposition of Organic Compounds and Microorganisms

英語

antifungal effect

2020-10

MDPI

Catalysts

10(10)

1194

Seven commercial titania (titanium(IV) oxide; TiO2) powders with different structural properties and crystalline compositions (anatase/rutile) were modified with copper by two variants of a photodeposition method, i.e., methanol dehydrogenation and water oxidation. The samples were characterized by diffuse reflectance spectroscopy (DRS), X-ray powder diffraction (XRD), scanning electron microscopy (SEM), energy-dispersive X-ray spectroscopy (EDS) and X-ray photoelectron spectroscopy (XPS). Although zero-valent copper was deposited on the surface of titania, oxidized forms of copper, post-formed in ambient conditions, were also detected in dried samples. All samples could absorb visible light (vis), due to localized surface plasmon resonance (LSPR) of zero-valent copper and by other copper species, including Cu2O, CuO and CuxO (x:1-2). The photocatalytic activities of samples were investigated under both ultraviolet (UV) and visible light irradiation (>450 nm) for oxidative decomposition of acetic acid. It was found that titania modification with copper significantly enhanced the photocatalytic activity, especially for anatase samples. The prolonged irradiation (from 1 to 5 h) during samples' preparation resulted in aggregation of copper deposits, thus being detrimental for vis activity. It is proposed that oxidized forms of copper are more active under vis irradiation than plasmonic one. Antimicrobial properties against bacteria (Escherichia coli) and fungi (Aspergillus niger) under vis irradiation and in the dark confirmed that Cu/TiO2 exhibits a high antibacterial effect, mainly due to the intrinsic activity of copper species.

学術雑誌論文

Version of Record

Creative Commons Attribution 4.0 International