Thermopower Modulation Analyses of High-Mobility Transparent Amorphous Oxide Semiconductor Thin-Film Transistors

英語

carrier relaxation time

2022-10-25

American Chemical Society

ACS Applied Electronic Materials

4(10)

5081-5086

Transparent amorphous oxide semiconductor InSnZnOx (ITZO)-based thin-film transistors (TFTs) exhibit a high field-effect mobility (mu FE). Although ITZO-TFTs have attracted increasing attention as a next-generation backplane of flat panel displays, the origin of the high mu FE remains unclear due to the lack of systematic quantitative analyses using thermopower (S) as the measure. Here, we show that the high mu FE originates from an extremely light carrier effective mass (m*) and a long carrier relaxation time (z). The S measurements of several ITZO films with different carrier concentrations clarified that m* of ITZO films is similar to 0.11 m0, which is similar to 70% of that of a commercial oxide semiconductor, amorphous InGaZnO4 (similar to 0.16 m0). We then fabricated bottom-gate-top-contact ITZO-TFTs displaying excellent transistor characteristics (mu FE similar to 58 cm2 V-1 s-1) using amorphous AlOx as the gate insulator and demonstrated that the effective thickness increases with the gate voltage. This suggests that the bulk predominantly contributes to the drain current, which results in z as long as similar to 3.6 fs, which is quadruple that of amorphous InGaZnO4-TFTs (similar to 0.9 fs). The present results are useful to further improve the mobility of ITZO-TFTs.

学術雑誌論文

Accepted Manuscript

This document is the Accepted Manuscript version of a Published Work that appeared in final form in [JournalTitle], copyright © American Chemical Society after peer review and technical editing by the publisher. To access the final edited and published work see https://pubs.acs.org/articlesonrequest/AOR-AKPAHP7A29ADCR9JGZNE