Controlled synthesis of LiNi0.5Mn1.5O4 cathode materials with superior electrochemical performance through urea-based solution combustion synthesis

英語

solution combustion synthesis

2015-05-29

Royal Society of Chemistry (RSC)

RSC advances

5(62)

49831-49837

High-voltage LiNi0.5Mn1.5O4 cathode materials were synthesized using urea-based solution combustion synthesis combined with a calcination treatment. The morphology and particle size distribution of the products were considerably dependent on the amount of urea fuel. The electrochemical characterization illustrated that the sample that was produced with a fuel ratio of phi = 0.5 had a homogenous particle size distribution of approximately 8 mu m, and showed the best cycling and rate performance. LiNi0.5Mn1.5O4 with two different structures of disordered Fd (3) over barm and ordered P4(3)32 were obtained by controlling the calcination process. The samples, which were calcined at 800 degrees C with fast cooling, presented a disordered structure of Fd (3) over barm, and the samples, which were calcined at 800 degrees C with slow cooling and reannealing at 600 degrees C, demonstrated an ordered structure of P4(3)32. The sample with a disordered structure exhibited a better electrochemical performance than the sample with an ordered structure. The disordered sample produced at phi = 0.5 presented a discharge capacity of 130.73 mA h g(-1) and a capacity retention of 98.43% after 100 cycles at 1 C. Even at a higher current rate of 3 C, the sample still showed a high discharge capacity of 117.79 mA h g(-1) and a capacity retention efficiency of 97.63% after 300 cycles.

学術雑誌論文

Accepted Manuscript

2046-2069