Corrosion of Al–Sn–Bi alloys in alcohols at high temperatures. Part II: Effect of anodizing on corrosion


Hokkaido University \| Library \| HUSCAP	Advanced Search		言語

	Home
	About HUSCAP
	Open Access Policy

	Browse by Author

Browse
	Communities & Collections

	Scholarly Journals
	Theses
	Doctoral Dissertations Listed by Graduate Schools
	Conference Procs.
	Events

	HUSCAP Senior (in Japanese)

	Societies

	Downloads (country)

For university staff
	How to post your papers to HUSCAP
	Publication of theses
	Helpline about theses publication

Open Archives Compliant

You can search our collection also at:
	Google
	Google Scholar
	CiNii
	IRDB
	OAIster
	NDLTD

Files in This Item:

kikuchi_CS52_2525-2534.pdf

3.66 MB

PDF

Please use this identifier to cite or link to this item:http://hdl.handle.net/2115/45097

Title:	Corrosion of Al–Sn–Bi alloys in alcohols at high temperatures. Part II: Effect of anodizing on corrosion
Authors:	Kikuchi, Tatsuya Browse this author
	Hara, Yasuhito Browse this author
	Sakairi, Masatoshi Browse this author
	Yonezawa, Tetsu Browse this author
	Yamauchi, Akira Browse this author
	Takahashi, Hideaki Browse this author
Keywords:	Aluminum alloy
	SEM
	Hot corrosion
Issue Date:	Aug-2010
Publisher:	Elsevier
Journal Title:	Corrosion Science
Volume:	52
Issue:	8
Start Page:	2525
End Page:	2534
Publisher DOI:	10.1016/j.corsci.2010.04.031
Abstract:	Nine kinds of Al alloys were anodized to form porous anodic oxide films, and then anodized specimens were immersed in 2-(2-(2-methoxyethoxy)ethoxy)ethanol (MEEE) and 2-(2-(2-butoxyethoxy)ethoxy)ethanol (BEEE) at 415 K. Al-1.0%Sn-1.0%Bi alloy was corroded severely in both BEEE and MEEE, whereas other 8 alloys showed no corrosion. The corrosion proceeded under the anodic oxide films through cracks formed in the film. Cathodic polarization in Cu electroplating solution after corrosion suggested that the crack formation during immersion in hot MEEE is due to thermal expansion of the substrate and Sn and Bi containing particles included in the anodic oxide film.
Relation:	http://www.sciencedirect.com
Type:	article (author version)
URI:	http://hdl.handle.net/2115/45097
Appears in Collections:	工学院・工学研究院 (Graduate School of Engineering / Faculty of Engineering) > 雑誌発表論文等 (Peer-reviewed Journal Articles, etc)

Submitter: 菊地竜也

OAI-PMH ( junii2 , jpcoar_1.0 )

- Hokkaido University