Photo-induced properties of non-annealed anatase TiO2 mesoporous film prepared by anodizing in the hot phosphate/glycerol electrolyte
Title: | Photo-induced properties of non-annealed anatase TiO2 mesoporous film prepared by anodizing in the hot phosphate/glycerol electrolyte |
Authors: | Taguchi, Yoshiaki Browse this author | Tsuji, Etsushi Browse this author | Aoki, Yoshitaka Browse this author →KAKEN DB | Habazaki, Hiroki Browse this author →KAKEN DB |
Keywords: | Anodic TiO2 mesoporous film | Non-annealing procedures | Phosphate/glycerol electrolyte | Photo-induced properties |
Issue Date: | 1-Oct-2012 |
Publisher: | Elsevier B.V. |
Journal Title: | Applied Surface Science |
Volume: | 258 |
Issue: | 24 |
Start Page: | 9810 |
End Page: | 9815 |
Publisher DOI: | 10.1016/j.apsusc.2012.06.035 |
Abstract: | In this study, anatase crystalline TiO2 mesoporous film were formed by anodizing of titanium specimens without annealing procedures. The specimens were anodized at 3 and 20 V in 0.6 mol dm^[-3] K2HPO4 and 0.2 mol dm^[-3] K3PO4/glycerol electrolyte at 433 K. The obtained films had mesoporous structures with pore diameters as small as ~10 nm. The mesoporous film formed at 20 V without annealing (MP-20V) was a mixture of amorphous phase and nanograined anatase, which clearly showed strong <001> preferred orientation, whereas that at 3 V was completely amorphous. Even without annealing, the MP-20V showed high photocatalytic activities for decomposition of water and methylene blue. In contrast, the anodic TiO2 nanotube film formed in NH4F/ethylene glycol electrolyte revealed photocatalytic activities only after annealing at 723 K, because of the amorphous nature of the as-anodized nanotube film. The MP-20V film also showed superhydrophilicity with UV light irradiation. |