TiB2-Based Composites for Ultra-High-Temperature Devices, Fabricated by SHS, Combining Strong and Weak Exothermic Reactions
This item is licensed under:Creative Commons Attribution 3.0 Unported
| Title: | TiB2-Based Composites for Ultra-High-Temperature Devices, Fabricated by SHS, Combining Strong and Weak Exothermic Reactions |
| Authors: | Ziemnicka-Sylwester, Marta Browse this author |
| Keywords: | TiB2 | | boron carbide | | ceramic matrix composites (CMCs) | | self-propagating high temperature synthesis (SHS) | | ultra-high temperature ceramics (UHTCs) |
| Issue Date: | 10-May-2013 |
| Publisher: | MDPI AG |
| Journal Title: | Materials |
| Volume: | 6 |
| Issue: | 5 |
| Start Page: | 1903 |
| End Page: | 1919 |
| Publisher DOI: | 10.3390/ma6051903 |
| Abstract: | TiB2-based ceramic matrix composites (CMCs) were fabricated using elemental powders of Ti, B and C. The self-propagating high temperature synthesis (SHS) was carried out for the highly exothermic "in situ" reaction of TiB2 formation and the "tailing" synthesis of boron carbide characterized by weak exothermicity. Two series of samples were fabricated, one of them being prepared with additional milling of raw materials. The effects of TiB2 vol fraction as well as grain size of reactant were investigated. The results revealed that combustion was not successful for a TiB2:B4C molar ratio of 0.96, which corresponds to 40 vol% of TiB2 in the composite, however the SHS reaction was initiated and self-propagated for the intended TiB2: B4C molar ratio of 2.16 or above. Finally B13C2 was formed as the matrix phase in each composite. Significant importance of the grain size of the C precursor with regard to the reaction completeness, which affected the microstructure homogeneity and hardness of investigated composites, was proved in this study. The grain size of Ti powder did not influence the microstructure of TiB2 grains. The best properties (HV = 25.5 GPa, average grain size of 9 mu m and homogenous microstructure), were obtained for material containing 80 vol% of TiB2, fabricated using a graphite precursor of (2) mu m. |
| Rights: | http://creativecommons.org/licenses/by/3.0/ |
| Type: | article |
| URI: | http://hdl.handle.net/2115/53048 |
| Appears in Collections: | 工学院・工学研究院 (Graduate School of Engineering / Faculty of Engineering) > 雑誌発表論文等 (Peer-reviewed Journal Articles, etc)
|
Submitter: Marta Ziemnicka-Sylwester
|