Low-temperature fabrication of NiCuZn Ferrite^|^ndash;(Ba0.7Sr0.3)TiO3 composites using granulated powders
Title: | Low-temperature fabrication of NiCuZn Ferrite^|^ndash;(Ba0.7Sr0.3)TiO3 composites using granulated powders |
Authors: | Kitahara, Naoto Browse this author | Kageyama, Hiroaki Browse this author | Kawasaki, Tomoya Browse this author | Abe, Kazutomo Browse this author | Itoh, Hidenobu Browse this author | Takahashi, Junichi Browse this author →KAKEN DB |
Keywords: | NiCuZn ferrite | (Ba0.7Sr0.3)TiO3 | Composite ceramics | Granulated powder | Bi2O3-based additive | Low-temperature sintering |
Issue Date: | 2013 |
Publisher: | The Ceramic Society of Japan |
Journal Title: | Journal of the Ceramic Society of Japan |
Volume: | 121 |
Issue: | 1409 |
Start Page: | 54 |
End Page: | 61 |
Publisher DOI: | 10.2109/jcersj2.121.54 |
Abstract: | NiCuZn ferrite( Ba0.7Sr0.3)TiO3 (BST) composite ceramics with the BST content of up to 50 vol% were fabricated by sintering compacted powder mixtures at 900°C. The granulation of the BST powder and addition of a Bi2O3-based oxide additive effectively assisted the densification of the composite samples. The samples thus fabricated showed required ¾r values whereas their ®r values were considerably reduced, especially for those with lower BSTcontents. From the detailed examinations on the effect of the Bi2O3- based oxide additives and on the process modification to improve the reduced ®r values, the addition of a Bi2O3ZnO additive with the eutectic composition of as low as 1wt%was enough to produce a densified 10 vol%BSTcomposite sample with a highest ®r value. It was also found that the incorporation of ferrite granules calcined at 600°C caused further improvement of ®r. Thus, a densified 10BST composite sample with ®r = 125 was fabricated by low-temperature sintering at 900°C. |