Advancing and receding contact angle investigations for highly sticky and slippery aluminum surfaces fabricated from nanostructured anodic oxide

This item is licensed under: Creative Commons Attribution 3.0 Unported

Files in This Item:
c8ra07712f.pdf1.33 MBPDFView/Open
c8ra07712f1.mp410.11 MBMP4 videoView/Open
Please use this identifier to cite or link to this item:http://hdl.handle.net/2115/72219

Title: Advancing and receding contact angle investigations for highly sticky and slippery aluminum surfaces fabricated from nanostructured anodic oxide
Authors: Nakajima, Daiki Browse this author
Kikuchi, Tatsuya Browse this author →KAKEN DB
Natsui, Shungo Browse this author →KAKEN DB
Suzuki, Ryosuke O. Browse this author →KAKEN DB
Issue Date: 2018
Publisher: Royal Society of Chemistry
Journal Title: RSC advances
Volume: 8
Issue: 65
Start Page: 37315
End Page: 37323
Publisher DOI: 10.1039/c8ra07712f
Abstract: The fabrication of sticky and slippery superhydrophobic aluminum was achieved by anodizing in pyrophosphoric acid and modification with self-assembled monolayers (SAMs). In addition, the corresponding sliding behaviors of a water droplet were investigated by contact angle measurements and direct observations. For the formation of anodic alumina nanofibers, 4N aluminum plates were anodized in a concentrated pyrophosphoric acid solution at 25-75 V. The morphology of the anodic oxide successively changed to barrier oxide, porous oxide, nanofibers, bundle structures with many nanofibers, and then weak nanofibers during anodizing. The anodized specimens were immersed in a fluorinated phosphonic acid/ethanol solution to form SAMs on the surface of the anodic oxide. The contact angle hysteresis drastically changed with anodizing time: it increased with the formation of porous oxide, decreased for the nanofibers and bundle structures, and then increased once again for the weak nanofibers. Correspondingly, the adhesion interaction between the water droplet and the aluminum surface also drastically changed to show sticky, slippery, and sticky behaviors with anodizing time. More sticky and slippery aluminum surfaces can be obtained by anodizing at higher voltages. The slippery behavior was further improved through two distinct anodizing processes with the formation of ordered alumina nanofibers. A superhydrophobic aluminum surface with coexisting sticky and slippery properties was fabricated by the selective anodizing method.
Rights: https://creativecommons.org/licenses/by/3.0/
Type: article
URI: http://hdl.handle.net/2115/72219
Appears in Collections:工学院・工学研究院 (Graduate School of Engineering / Faculty of Engineering) > 雑誌発表論文等 (Peer-reviewed Journal Articles, etc)

Submitter: 菊地 竜也

Export metadata:

OAI-PMH ( junii2 , jpcoar )

MathJax is now OFF:


 

 - Hokkaido University