Al-Crめっきの前処理としてのTiAlのアノード溶解

Files in This Item:
54_363.pdf879.6 kBPDFView/Open
Please use this identifier to cite or link to this item:http://hdl.handle.net/2115/74936

Title: Al-Crめっきの前処理としてのTiAlのアノード溶解
Other Titles: Anodic Dissolution of TiAl Surface as a Pretreatment for Al-Cr Electroplating
Authors: 上田, 幹人1 Browse this author →KAKEN DB
薄田, 大吾2 Browse this author
近田, 昭一3 Browse this author
大塚, 俊明4 Browse this author
Authors(alt): Ueda, Mikito1
Susukida, Daigo2
Konda, Shouichi3
Ohtsuka, Toshiaki4
Keywords: Al-Cr Alloy
Molten Salt
TiAl
High Temperature Oxidation
Issue Date: May-2003
Publisher: 表面技術協会
Journal Title: 表面技術
Journal Title(alt): Journal of The Surface Finishing Society of Japan
Volume: 54
Issue: 5
Start Page: 363
End Page: 366
Publisher DOI: 10.4139/sfj.54.363
Abstract: Anodic stripping of TiAl surface was carried out in AlCl3-NaCl-KCl molten salt at 423 K as a pretreatment for the deposit formation of an Al-Cr alloy layer. The Al-Cr alloy deposit on the TiAl significantly improved the corrosion resistance against high temperature oxidation. In anodic stripping at 0.4 V vs. Al/Al3+, anodic dissolution of surface occurred non-uniformly. On the other hand, an oxide film on TiAl was completely removed by uniform anodic dissolution at 1.2 V with electricity of 1 C cm-2. An Al-Cr electroplating layer that was formed after the anodic stripping at 1.2 V, exhibited excellent oxidation resistance that was confirmed by an oxidation test at 1173 K for 24 h.
Type: article
URI: http://hdl.handle.net/2115/74936
Appears in Collections:工学院・工学研究院 (Graduate School of Engineering / Faculty of Engineering) > 雑誌発表論文等 (Peer-reviewed Journal Articles, etc)

Submitter: 上田 幹人

Export metadata:

OAI-PMH ( junii2 , jpcoar_1.0 )

MathJax is now OFF:


 

 - Hokkaido University