酸化鉄触媒添加コークスの反応挙動
| Title: | 酸化鉄触媒添加コークスの反応挙動 |
| Other Titles: | Reaction Behavior of Coke with Iron Oxide Catalyst |
| Authors: | 山本, 雄一郎1 Browse this author | | 柏谷, 悦章2 Browse this author | | 三浦, 誠司3 Browse this author →KAKEN DB | | 西村, 勝4 Browse this author | | 加藤, 健次5 Browse this author | | 野村, 誠治6 Browse this author | | 窪田, 征弘7 Browse this author | | 国友, 和也8 Browse this author | | 内藤, 誠章9 Browse this author |
| Authors(alt): | Yamamoto, Yuichiro1 | | Kashiwaya, Yoshiaki2 | | Miura, Seiji3 | | Nishimura, Masaru4 | | Katou, Kenji5 | | Nomura, Seiji6 | | Kubota, Masahiro7 | | Kunitomo, Kazuya8 | | Naito, Masaaki9 |
| Keywords: | coke gasification | | iron oxide catalyst | | μ-X-ray CT | | coke degradation | | nondestructive analysis | | integrated image processing |
| Issue Date: | 1-May-2010 |
| Publisher: | 日本鉄鋼協会 |
| Journal Title: | 鉄と鋼 |
| Volume: | 96 |
| Issue: | 5 |
| Start Page: | 288 |
| End Page: | 296 |
| Publisher DOI: | 10.2355/tetsutohagane.96.288 |
| Abstract: | The performance of coke in blast furnace (BF) used to prefer a high strength and low reactivity, generally, while the high reactivity coke commonly has a low strength. To overcome the contradiction, we are going to use the catalytic effect on the coke gasification. It is important to clarify the mechanism of coke gasification concerning to the coke microstructure and pore. In this study, the coke gasification was analyzed using μ-X-ray CT (Computed Tomography). The optimum conditions for the image processing of the data from the X-ray CT were obtained through the comparison with the cross section of the coke embedded in a resin. Nondestructive observation became possible. To improve resolution of the nondestructive observation, the sample shape was changed from spherical to cylindrical one and the observation conditions were adjusted to an optimum one. It was found that the resolution of the nondestructive observation of cylindrical sample was better than that of spherical sample. Using high precision μ-X-ray CT, the position of the catalyst added and the reaction behavior became clear. Furthermore, using new developed image processing of the data from the μ-X-ray CT, macroscopic reaction behavior of the catalyst became clear. |
| Type: | article |
| URI: | http://hdl.handle.net/2115/75171 |
| Appears in Collections: | 工学院・工学研究院 (Graduate School of Engineering / Faculty of Engineering) > 雑誌発表論文等 (Peer-reviewed Journal Articles, etc)
|