Increased Production and Molecular Weight of Artificial Polyhydroxyalkanoate Poly(2-hydroxybutyrate) Above the Glass Transition Temperature Threshold
This item is licensed under:Creative Commons Attribution 4.0 International
Title: | Increased Production and Molecular Weight of Artificial Polyhydroxyalkanoate Poly(2-hydroxybutyrate) Above the Glass Transition Temperature Threshold |
Authors: | Matsumoto, Ken'ichiro Browse this author →KAKEN DB | Kageyama, Yuki Browse this author |
Keywords: | biobased plastic | polyester | enzymatic synthesis | lactate-polymerizing enzyme | artificial biopolymer |
Issue Date: | 24-Jul-2019 |
Publisher: | Frontiers Media |
Journal Title: | Frontiers in bioengineering and biotechnology |
Volume: | 7 |
Start Page: | 177 |
Publisher DOI: | 10.3389/fbioe.2019.00177 |
Abstract: | Poly(2-hydroxybutyrate) [P(2HB)] is an artificial polyhydroxyalkanoate (PHA) synthesized using engineered 2-hydroxyalkanoate-polymerizing PHA synthase. In the present study, the effect of temperature on P(2HB) synthesis was investigated. Recombinant Escherichia coli harboring PHA synthetic genes were cultivated with 2HB and 3-hydroxybutyrate (3HB) supplementation at varied temperatures ranging from 24 to 36 degrees C for the synthesis of P(2HB) and natural PHA P(3HB), respectively. P(2HB) production and its molecular weight increased considerably at a threshold temperature of 32-34 degrees C. The trend was not observed during the synthesis of P(3HB). Notably, the threshold temperature was close to the glass transition temperature (T-g) of P(2HB) (30 degrees C), while the T-g of P(3HB) (4 degrees C) was much lower than the cultivation temperature. The results suggest that thermal motion of the polymer chains influenced the production and molecular weight of the obtained polymer. According to the results, the production and molecular weight of PHA drastically changes at the threshold temperature, which is linked to the T-g of the polymer. The hypothesis should be applicable to PHAs in general, and potentially explains the inability to biosynthesize high-molecular-weight polylactate homopolymer with a T-g of 60 degrees C. |
Rights: | https://creativecommons.org/licenses/by/4.0/ |
Type: | article |
URI: | http://hdl.handle.net/2115/75275 |
Appears in Collections: | 工学院・工学研究院 (Graduate School of Engineering / Faculty of Engineering) > 雑誌発表論文等 (Peer-reviewed Journal Articles, etc)
|
|