High-temperature Oxidation Behavior of 9Cr Ferritic-steel in Carbon Dioxide

Files in This Item:
ISIJ Int. 54(6)_ 1379-1385.pdf1.26 MBPDFView/Open
Please use this identifier to cite or link to this item:http://hdl.handle.net/2115/76358

Title: High-temperature Oxidation Behavior of 9Cr Ferritic-steel in Carbon Dioxide
Authors: Kaya, Keitarou Browse this author
Hayashi, Shigenari Browse this author →KAKEN DB
Ukai, Shigeharu Browse this author →KAKEN DB
Keywords: high-temperature oxidation
carburization
Carbon dioxide
ferritic steel
oxyfuel combustion
Issue Date: 15-Jun-2014
Publisher: Iron and Steel Institute of Japan
Journal Title: ISIJ International
Volume: 54
Issue: 6
Start Page: 1379
End Page: 1385
Publisher DOI: 10.2355/isijinternational.54.1379
Abstract: Commercial STBA26, 9Cr-1Mo ferritic steel, was exposed to CO2 gas and air at 700°C in order to understand the oxidation behavior of a 9Cr-steel in CO2 atmosphere. Oxidation of STBA26 was significantly accelerated in CO2 compared to that in air. In CO2 thick iron rich oxide nodules were formed on the steel and chromium rich carbides were found to form below the oxide scale. The carbon activity at the scale/alloy interface was sufficiently high to maintain parabolic internal continuous carbon supply to the interface is considered to be a reason to cause a breakaway of protective oxide scale.
Rights: 著作権は日本鉄鋼協会にある
Type: article
URI: http://hdl.handle.net/2115/76358
Appears in Collections:工学院・工学研究院 (Graduate School of Engineering / Faculty of Engineering) > 雑誌発表論文等 (Peer-reviewed Journal Articles, etc)

Submitter: 林 重成

Export metadata:

OAI-PMH ( junii2 , jpcoar_1.0 )

MathJax is now OFF:


 

 - Hokkaido University