TiAl合金の高温変形挙動に及ぼす耐酸化コーティングの影響

Files in This Item:
J. Jpn Inst. Met. Mater. 71(1) 25.pdf2.07 MBPDFView/Open
Please use this identifier to cite or link to this item:http://hdl.handle.net/2115/76569

Title: TiAl合金の高温変形挙動に及ぼす耐酸化コーティングの影響
Other Titles: Effect of Oxidation Resistant Coatings on the Deformation Behavior of TiAl Alloys at 1173 K in Air
Authors: 西本, 工1 Browse this author
林, 重成2 Browse this author →KAKEN DB
成田, 敏夫3 Browse this author
Authors(alt): Nishimoto, Takumi1
Hayashi, Shigenari2
Narita, Toshio3
Keywords: titanium aluminides
oxidation
coatings
mechanical property at high temperature
Issue Date: Jan-2007
Publisher: 日本金属学会
Journal Title: 日本金属学会誌
Journal Title(alt): Journal of the Japan Institute of Metals
Volume: 71
Issue: 1
Start Page: 25
End Page: 33
Publisher DOI: 10.2320/jinstmet.71.25
Abstract: The effects of coatings on the deformation and oxidation behavior of Ti-50Al alloy were investigated at 1173 K in air at a constant loading of 30 MPa. The coating was formed by a two-step Cr/Al diffusion treatment and consisted of an outermost TiAl2 layer, an outer Al-rich γ layer, an intermediate γ, Laves and β mixed layer, and a Cr diffusion zone. Tensile tests were also carried out with sole Cr or Al coated TiAl and uncoated TiAl at 1173 K for comparison purposes. The oxide scales formed on the uncoated TiAl and the sole Cr coated specimens were a mixture of TiO2 and Al2O3, which displayed extensive exfoliation. Both the two-step Cr/Al coated TiAl and the sole Al coated specimens formed a protective Al2O3 layer and little oxide exfoliation was observed here. Significant cracks were observed in the sole Al coated TiAl, while no cracks were observed in the sole Cr coated TiAl; the two-step Cr/Al coated TiAl showed a number of cracks in the coatings. Low creep rates in the two-step Cr/Al coated TiAl could be due to the Laves phase with a hexagonal C14 structure in the intermediate, γ, β and Laves phase mixture, and the high creep rates of the sole Cr coated TiAl may originate in the major β phase component with a B2 structure in the γ, β, and Laves phase mixture.
Type: article
URI: http://hdl.handle.net/2115/76569
Appears in Collections:工学院・工学研究院 (Graduate School of Engineering / Faculty of Engineering) > 雑誌発表論文等 (Peer-reviewed Journal Articles, etc)

Submitter: 林 重成

Export metadata:

OAI-PMH ( junii2 , jpcoar )

MathJax is now OFF:


 

 - Hokkaido University